Cause analysis and solution of plastic shell dent

Release time:2022-02-28

During the injection molding process, the dents of the plastic shell are shrinkage dents generated after the plastic is cooled and hardened, which mainly appear in the thick wall of the plastic shell, ribs, shell, nut insert back, etc.

3.jpg


1、 Equipment:

(1) Insufficient feeding

The screw or plunger is seriously worn, and the molten material leaks during the injection and pressure maintaining process, which reduces the mold filling pressure and the amount of molten material, resulting in insufficient molten material.


(2) Nozzle hole too large or too small

If it is too small, it is easy to block the sprue; if it is too large, the injection force is small, and it is difficult to fill the mold.


2、 Mold:

(1) The gate is too small or the runner is too narrow or shallow, the runner efficiency is low, the resistance is large, and the molten material is cooled too early.

The gate cannot be too large, otherwise the shear rate will be lost, the material viscosity is high, and the plastic shell will not be full. The gate should be opened on the thick wall of the plastic shell. By setting up a cold charging well with sufficient capacity in the flow channel, the cold charging can be excluded from entering the mold cavity, so that the mold filling can continue.

The gate length of point gate and needle gate must be controlled below 1mm, otherwise the plastic will solidify rapidly in the gate, affecting the pressure transmission; If necessary, increase the number of point gates or gate positions to meet the actual needs; When the flow passage is long and thick, exhaust grooves should be set at the edge of the flow passage to reduce the blocking effect of air on the flow of materials.


(2) Multi gate mold should adjust the filling speed of each gate, and it is best to set up gates symmetrically.


(3) The key parts of the mold should be effectively set with cooling channels to ensure that the cooling of the mold has a good effect on removing or reducing shrinkage cavities.


(4) The whole mold should be free of burrs, have reliable mold closing tightness, and can withstand the filling of high-pressure, high-speed, low viscosity molten materials.


3、 Technical aspects:

(1) Increase the injection pressure, maintain the pressure and prolong the injection time.

For plastic with high fluidity, high pressure will cause flash and collapse, so the material temperature should be appropriately reduced, and the temperature of the front of the barrel and the nozzle should be reduced, so that the volume change of molten material entering the cavity is reduced, and it is easy to cold solidify; For high viscosity plastics, the barrel temperature should be increased to make it easier to fill the mold. When the gate area shrinks, the pressure holding time should be extended.


(2) Increasing the injection speed can easily fill the parts and remove most of the shrinkage.


(3) The thin-walled plastic shell should increase the mold temperature to ensure the smooth flow of materials; The thick wall plastic shell should reduce the mold temperature to accelerate the curing and shaping of the skin.


(4) The cooling residence time of the plastic shell in the mold is prolonged, the production cycle is kept uniform, the back pressure is increased, and a certain buffer pad is reserved at the front end of the screw, which is conducive to reducing the shrinkage phenomenon.


(5) The low precision plastic shell should be taken out of the mold as soon as possible and cooled slowly in air or hot water, so that the shrinkage depression can become smooth without affecting the use.


4、 Raw materials:

The raw material is too soft and easy to flow. The effective way is to add nucleating agent to the plastic to accelerate crystallization.


5、 Plastic shell design:

The design of plastic shell should make the wall thickness uniform and try to avoid the change of wall thickness. For plastics with large shrinkage such as polypropylene, when the thickness changes by more than 50%, it is best to replace the thickened part with ribs.

Copyright: Shenzhen Zhongyuan Plastic Co., Ltd. | mold processing customized manufacturer. If you want to know the processing price of the factory, how much is it, and which is good, please contact us Yue ICP Bei No. 17060480
主站蜘蛛池模板: 日韩高清在线播放不卡 | 天天干视频网站 | 日本免费专区 | 五月婷婷在线播放 | 野外三级国产在线观看 | 婷婷综合缴情亚洲五月伊 | 深夜爽爽福利gif在线观看 | 视频大全在线观看免费 | 天堂资源在线8 | 一级女人18毛片免费 | 亚洲偷 | 亚洲视频在线免费看 | 日韩精品综合 | 亚洲天堂资源网 | 在线观看视频国产 | 片成年免费观看网站黄 | 青青草原伊人网 | 天天曰夜夜曰 | 日韩日b| 日韩 欧美 中文字幕 不卡 | 午夜视频在线观看完整版 | 亚洲图片综合区另类图片 | 日韩欧美精品综合久久 | 污在线视频 | 午夜999| 五月天丁香婷婷综合 | 天天躁夜夜躁很很躁麻豆 | 亚洲高清资源在线观看 | 日本成人在线网站 | 最近免费韩国高清在线观看 | 欧美亚洲国产一区 | 三级香蕉 | 欧美又肥又胖的大bbwⅹ | 亚洲国产日韩欧美在线a乱码 | 日本一区免费在线 | 特级黄 | 日本精品视频在线 | 欧美一级做一级爱a做片性 欧美一级做一a做片性视频 | 日韩综合在线视频 | 欧美性第一页 | 日韩高清免费在线观看 |